Backstand and contact wheel grit 60 and diameter 40

A big balisong, 24cm long, 11,5 cm sharp, 115w8, differential hardening, toxified Gr5 Ti handle. Carbon fiber spacer, build on CC bearing.

Thank you very much :D

thank you :D

Yes i hammered then, now i try to make a mushroom head on each side :D. that is not maybe perfectly straight, but as i make the tang cup one by one i can adjust :D

thank you :) 40 or 60mm contact wheel. I make a flat grind and after that i grind with the contact wheel.

Thank you guys:D

Thank you Mike :D

Thank you. It's not a good flipper, it's a bit too light. But it's possible to flip with :D

A small compact balisong. 115w8, 2.7 mm thick blade, chaotic hamon, 6.5 cm sharp, 17.6 cm long open for 10.5 cm closed. 9mm thick and 12mm thick to the pivot screw. Handle, latch, tlatch and tang pin are Ta6V4 (Ti gr5). It's a friction latch, build as my friction folder. No mechanism, only...

thank you :D

Mainly an EDC ultra light . 115w8 differential hardening, 2.7mm thick. 10 cm sharp. 22 cm long. Red G10 handle, black G10 for the spacer, copper pin, annealed 100c6 tang pins.

Thank you very much :D

C130 blade for more or less 6/8 blade. More or less 3" sharp. Brass folded handle.

A small kamisori i did to complete 2014. C130 water hardened, 220°c tempering (2 times). Stab linen wrapping . More or less a 5/8 for more or less 50-55mm honed. The shave is not bad at all :D

Yes i use a 00 checkering file for the tang (a bit polished because it was a bit too rough :D In europe, guys enjoy the wood, in usa it's hard wood, or something more technical as g10, carbon fiber. Copper is good to have a vintage look, but it's not traditionnal at all. Horn, bone, ivory and...

A straight razor 5/8, c130 steel, differential water hardened blade, double tempering to 200°c. Near wedge, vintage completion. Plumbery copper tube cut and solder to have a very basic scale, fastly done and fully efficient in the way of the vintage blade. The copper is hammered and bead blasted...

Just a bit more of carbone, and a bit more or tungsten. Less chrome indeed, same manganese, same silicium quantity. That is mainly the amount of tungstène and the carbone quantity. It make really hard and tough edge, but it don't chip at all. The 1.2442 is and old steel use to make industrial...

A Halloween Straight Razor, C130, water hardened, double tempering to 200°c, 3" sharp, 6./8 , halloween g10 and Ta6V4 spacer.

Yes achim is the guy to contact for the sc145. I stopped to use 1.2519 since i use 1.2442 . That steel is less tough and sharp than any other tool steel for me :) even the 1.2519 which was my favorite was beaten by the 115w8 :D For the sc145 that is the supplyer :D For the price of the 1.2442...