Quick and simple question.
I have a blade made from 1095 that warped on me... I plan on tempering at 500 degrees 2 times. Can I staighten the blade durning the 2nd tempering cycle of/at 500 degrees ? Or would it be better to normalize striaghten - re heat the blade and re quench?
I have a blade made from 1095 that warped on me... I plan on tempering at 500 degrees 2 times. Can I staighten the blade durning the 2nd tempering cycle of/at 500 degrees ? Or would it be better to normalize striaghten - re heat the blade and re quench?