Hello,
I recently put together a pid controller in a small tool box and can finally get a read out of what temps I actually have in my 2 brick forge. It is essentially a copy of Len Lunstroms(spelling?).
I was watching the temperature stabilize at say 1475 and it would stay there for a few minutes( or so it seemed to me), then it would start creeping either up or down. I did have an oscillating fan on, but I turned it off and nothing changed
I have a mini side arm burner on that forge. I am wondering if my 0 to 60 PSI regulator could be the problem or something else. The regulator is ancient and who knows what kind of shape the diafragms are in.
Any advice happily accepted.
Fred
I recently put together a pid controller in a small tool box and can finally get a read out of what temps I actually have in my 2 brick forge. It is essentially a copy of Len Lunstroms(spelling?).
I was watching the temperature stabilize at say 1475 and it would stay there for a few minutes( or so it seemed to me), then it would start creeping either up or down. I did have an oscillating fan on, but I turned it off and nothing changed
I have a mini side arm burner on that forge. I am wondering if my 0 to 60 PSI regulator could be the problem or something else. The regulator is ancient and who knows what kind of shape the diafragms are in.
Any advice happily accepted.